Polyhydroxybutyrate-based osteoinductive mineralized electrospun structures that mimic components and tissue...

Scaffolds for bone tissue engineering should enable regeneration of bone tissues with its native hierarchically organized extracellular matrix (ECM) and multiple tissue interfaces. To achieve this, inspired by the structure and properties of bone osteon, we fabricated polyhydroxybutyrate (PHB)-based mineralized electrospun fibrous scaffolds. After studying multiple PHB-based fibers, we chose 7%PHB/1%Gelatin fibers (PG) to fabricate mineralized fibers that mimic mineralized collagen fibers in bone. The mineralized PG (mPG) surface had a rough, hydrophilic layer of low crystalline calcium phosphate which was biocompatible to bone marrow stromal cells (BMSCs), induced their proliferation and was osteoinductive. Subsequently, by modulating the electrospinning process, we fabricated mPG-based novel higher order fibrous scaffolds that mimic the macroscale geometries of osteons of bone ECM. Inspired by the aligned collagen fibers in bone lamellae, we fabricated mPG scaffolds with aligned fibers that could direct anisotropic elongation of mouse BMSC (mBMSCs). Further, we fabricated electrospun mPG-based osteoinductive tubular constructs which can mimic cylindrical bone components like osteons or lamellae or be used as long bone analogues based on their dimensions. Finally, to regenerate tissue interfaces in bone, we introduced a novel bi-layered scaffold-based approach. An electrospun bi-layered tubular construct that had PG in the outer layer and 7%PHB/0.5%Polypyrrole fibers (PPy) in the inner layer was fabricated. The bi-layered tubular construct underwent preferential surface mineralization only on its outer layer. This outer mineralized layer supported osteogenesis while the inner PPy layer could support neural cell growth. Thus, the bi-layered tubular construct may be used to regenerate haversian canal in the osteons which hosts nerve fibers. Overall, the study introduced novel techniques to fabricate biomimetic structures that can regenerate components of bone osteon and its multiple tissue interfaces. The study lays foundation for the fabrication of a modular scaffold that can regenerate bone with its hierarchical structure and complex tissue interfaces.