Effect of Different Primers on Shear Bond Strength of Base Metal Alloys and Zirconia Frameworks

Ensuring a secure bond between a framework structure and layering composite resin veneer is essential for a long-lasting dental restoration. A variety of primer systems are available to facilitate the adhesive bonding. Nevertheless, the growing preference for efficiency and simplicity in dentistry has made the one-bottle universal primers a desirable option. This study aims to compare the effectiveness of universal primers on the shear bond strength (SBS) of base metal alloy (BMA) and zirconia to layering composite resin. Each 160 BMA and zirconia 20 × 10 × 5 mm test specimen was fabricated. Eight different primers (SunCera Metal Primer, Metal Primer Z, Reliance Metal Primer, Alloy Primer, MKZ Primer, Monobond Plus, ArtPrime Plus, and Clearfil Ceramic Primer Plus) were applied to 20 specimens in each group. Subsequently, a 5 × 2 mm composite resin build-up was applied. SBS tests were performed after 24 h of water storage and after thermocycling (25,000 cycles, 5-55 °C). On BMA, after water storage for 24 h, the bond strength values ranged from 26.53 ± 3.28 MPa (Metal Primer Z) to 29.72 ± 2.00 MPa (MKZ Primer), while after thermocycling, bond strength values ranged from 25.19 ± 1.73 MPa (MKZ Primer) to 27.69 ± 2.37 MPa (Clearfil Ceramic Primer Plus). On a zirconia base, after 24 h, the bond strengths values ranged from 22.63 ± 2.28 MPa (Reliance Primer) to 29.96 ± 2.37 MPa (MKZ Primer) and from 23.77 ± 3.86 MPa (Metal Primer Z) to 28.88 ± 3.09 MPa (Monobond Plus) after thermocycling. While no significant difference in bond strength was found between the primers on the BMA base, five primer combinations differed significantly from each other on zirconia (p = 0.002-0.043). All primers achieved a bond strength greater than 23 MPa on both framework materials after thermocycling. Thus, all primers tested can be applied to both framework materials with comparable results.