Aluminum-containing deposits are pervasive in drinking water distribution systems (DWDSs). However, the mechanisms driving dissolved Al transformation to pipe deposits remain elusive. This study investigated dissolved Al accumulation in DWDSs by batch experiments and long-term pipe experiments using actual finished water. PVC pipe experiments showed that dissolved Al hardly deposited on clean PVC pipe walls at alkaline pH. However, it could be substantially anchored by the pipe surface covered with Mn and Fe deposits formed from Mn(II) oxidation and Fe(III) precipitation. Batch experiments verified that the synthesized Mn and Fe oxides exhibited a strong capacity for dissolved Al uptake at pH 7.7 and 9.0 (dissolved Al was the dominant form). Biofilms on pipe walls also enhanced dissolved Al accumulation. Iron pipe experiments showed that corroded iron pipes with abundant iron corrosion products readily accumulated Al. Compared to chlorination and chloramination, non-disinfected conditions were more favorable for particulate Al deposition on iron pipe surface, probably due to Al immobilization by biofilms. In addition, continuous Al accumulation in iron pipes enhanced Fe release to pipe water. This study highlighted the important role of metal oxides in dissolved Al accumulation in DWDSs with abundant Mn and Fe solids, which provided new insights into deposit formation and control strategies.