Evaluating and Comparing Flexure Strength of Dental Models Printed Using Fused Deposition Modelling, Digital Light...

The introduction of three-dimensional (3D) printing in dentistry has mainly focused on applications such as surgical planning, computer-guided templates, and digital impression conversions. Additive manufacturing (AM), also known as 3D printing, involves layering resin material sequentially to construct objects and is gaining recognition for its role in creating custom-made medical appliances. The field of orthodontics has also embraced this technological wave and with the advent of cost-effective printers and biocompatible resins, 3D printing has become increasingly feasible and popular in orthodontic clinics. The limitations of traditional plaster models may have prompted the emergence of 3D-printed models, but it led to enhancing treatment planning and device fabrication, particularly in orthodontics. Notable desktop printing technologies include fused deposition modelling (FDM), digital light processing (DLP), and stereolithography (SLA), each employing distinct methods and materials for fabricating appliances. Evaluating mechanical properties, like flexure strength, is crucial to determine the material's ability to withstand bending forces and thus prove useful in fabricating thermoformable appliances, surgical templates, etc. This study aims to assess the flexure strength of 3D-printed models using FDM, DLP, and SLA technology, providing insights into their suitability as replacements for conventional models and shedding some light on the durability and sustainability of 3D-printed models.

Cuboids measuring 20 x 5 x 2 mm were cut from models, creating 10 samples per printer group. These samples underwent flexure strength testing using a three-point bending system in a universal testing machine.

The FDM group exhibited the highest flexure strength at 69.36 ± 6.03 MPa, while the DLP group showed the lowest flexure strength at 67.47 ± 20.58 MPa. The results can be attributed to the differences in resin materials used for fabrication, with FDM using acrylonitrile butadiene styrene (ABS) polymer and SLA/DLP using polymethyl methacrylate (PMMA), and also to the variation in their printing mechanism.

The findings affirm the suitability of FDM models for orthodontic applications, suggesting enhanced efficiency and reliability in clinical practices.