A Facile and Eco-friendly Route to Fabricate PolyLactic Acid Scaffolds with Graded Pore Size
Published on: October 17, 2016
[Study on NaOH improving the surface morphology of three-dimensional printed poly- L- lactic acid mesh scaffolds]
Hui Zeng1, Fang Guo1, Shuo Huang1
1Research Center of Tooth and Maxillofacial Tissue Regeneration and Restoration, School of Stomatology, Xi'an Medical University, Xi'an Shaanxi, 710021, P. R. China.
Objective:
To explore the effect of NaOH on the surface morphology of three-dimensional (3D) printed poly- L-lactic acid (PLLA) mesh scaffolds.
Methods:
The 3D printed PLLA mesh scaffolds were prepared by fused deposition molding technology, then the scaffold surfaces were etched with the NaOH solution. The concentrations of NaOH solution were 0.01, 0.1, 0.5, 1.0, and 3.0 mol/L, and the treatment time was 1, 3, 6, 9, and 12 hours, respectively. There were a total of 25 concentration and time combinations. After treatment, the microstructure, energy spectrum, roughness, hydrophilicity, compressive strength, as well as cell adhesion and proliferation of the scaffolds were observed. The untreated scaffolds were used as a normal control.
Results:
3D printed PLLA mesh scaffolds were successfully prepared by using fused deposition molding technology. After NaOH etching treatment, a rough or micro porous structure was constructed on the surface of the scaffold, and with the increase of NaOH concentration and treatment time, the size and density of the pores increased. The characterization of the scaffolds by energy dispersive spectroscopy showed that the crystal contains two elements, Na and O. The surface roughness of NaOH treated scaffolds significantly increased ( P<0.05) and the contact angle significantly decreased ( P<0.05) compared to untreated scaffolds. There was no significant difference in compressive strength between the untreated scaffolds and treated scaffolds under conditions of 0.1 mol/L/12 h and 1.0 mol/L/3 h ( P>0.05), while the compression strength of the other treated scaffolds were significantly lower than that of the untreated scaffolds ( P<0.05). After co-culturing the cells with the scaffold, NaOH treatment resulted in an increase in the number of cells on the surface of the scaffold and the spreading area of individual cells, and more synapses extending from adherent cells.
Conclusion:
NaOH treatment is beneficial for increasing the surface hydrophilicity and cell adhesion of 3D printed PLLA mesh scaffolds.