Hollow CoP/carbon as an efficient catalyst for the peroxymonosulfate activation derived from phytic acid assisted...

The catalyst's composition and rationally designed structure is significantly interlinked with its performance for wastewater remediation. Here, a novel hollow cobalt phosphides/carbon (HCoP/C) as an efficient catalyst for activating peroxymonosulfate (PMS) was prepared. The ZIF-67 was synthesized first, followed by phytic acid (PA) etching and then heat treatment was used to get HCoP/C. The PA was used as an etching agent and a source of phosphorus to prepare HCoP/C. To analyze catalytic performance, another solid cobalt phosphides/carbon (SCoP/C) catalyst was prepared for comparison. In contrast to SCoP/C, the HCoP/C exhibited higher catalytic efficiency when used to activate PMS to degrade Bisphenol A (BPA). The results showed that about 98 % of targeted pollutant BPA was removed from the system in 6 min with a rate constant of 0.78 min^-1, which was 4 times higher than the solid structure catalyst. The higher catalytic performance of HCoP/C is attributed to its hollow structure. In the study, other parameters such as BPA concentration, temperature, pH, and different catalyst amount were also tested. Moreover, the electron paramagnetic resonance (EPR) and radical quenching analysis confirmed that sulfate radicals were dominant in the HCoP/C/PMS system.