Synthesis of castor oil/PEG as textile softener

New castor oil/polyethylene glycol (CAO/PEG) hybrids were synthesized by reacting of CAO with PEG 300, 600, 1000, 2000 or 4000, in presence of ammonium per sulfate (APS) as an initiator. The optimum conditions to synthesis such hybrids are: PEG/CAO weight ratio, 35%; APS/PEG weight ratio, 15%; reaction temperature, 80 °C; and reaction time, 60 min. Only the hybrids based on PEG 1000 and 2000 formed oil in water stable emulsions. Treating cotton fabric samples with easy care finishing formulation containing 40 g/L of the synthesized hybrids emulsions results in an enhancement in softness, tensile strength, whiteness index, and stiffness along with a reduction in nitrogen content, wrinkle recovery angle, and wettability properties of treated fabric, compared to that sample finished in absence of that emulsions. The chemical structure of the synthesized CAO/PEG1000 hybrid was confirmed via the FTIR and ¹HNMRanalysis whereas the TEM analysis showed that the particles size of that hybrid emulsion is in the range of 27-105 nm. Moreover, such hybrid emulsion treated fabric surface was characterized via SEM and EDX analysis. Furthermore, treating dyed samples with the nominated hybrid emulsion improves the color strength of that samples but keeps the washing fastness, wet rubbing fastness as well as alkaline perspiration fastness of the dyed/finished samples unchanged. The wet rubbing fastness and alkaline perspiration fastness of all the dyed/finished samples were enhanced while the light fastness of such samples decreased.