Vacuum Plasma Treatment Device for Enhancing Fibroblast Activity on Machined and Rough Titanium Surfaces

This study was conducted to compare the effects of an innovative plasma surface treatment device that does not need a gas supply for titanium disks with two different surface topographies: the prototypical machined surface (MAC) and one of the most diffused roughened ones (SL) obtained through grit blasting and acid etching. A total of 200-MAC and 200-SL titanium disks were used. Each group of disks was divided into four sub-groups of 40 samples each that were subjected to five different tests. Among these, 150-MAC and 150-SL were considered the test group, and they were treated with plasma for 15, 30, and 60 s after being removed from the sterile packaging. On the other hand, 50-MAC and 50-SL were considered the control group, and they were only removed from sterile plastic vials. The samples were analyzed to evaluate the capability of the plasma treatment in influencing protein adsorption, cell adhesion, proliferation, and microbial growth on the test group disks when compared to the untreated disks. Protein adsorption was significantly enhanced after 20 min of plasma treatment for 15 and 30 s on the MAC and SL disks. Plasma treatment for 15 and 30 s significantly increased the level of adhesion in both treated samples after 30 min. Furthermore, the MAC samples showed a significant increase in cell adhesion 4 h after plasma treatment for 15 s. The SEM analysis highlighted that, on the treated samples (especially on the MAC disks), the cells with a polygonal and flat shape prevailed, while the fusiform- and globular-shaped cells were rare. The encouraging results obtained further confirm the effectiveness of plasma treatments on cell adhesion and fibroblast activity.