Chelating Additive Regulating Zn-Ion Solvation Chemistry for Highly Efficient Aqueous Zinc-Metal Battery

Aqueous zinc-metal batteries (AZMBs) usually suffered from poor reversibility and limited lifespan because of serious water induced side-reactions, hydrogen evolution reactions (HER) and rampant zinc (Zn) dendrite growth. Reducing the content of water molecules within Zn-ion solvation sheaths can effectively suppress those inherent defects of AZMBs. In this work, we originally discovered that the two carbonyl groups of N-Acetyl-ϵ-caprolactam (N-ac) chelating ligand can serve as dual solvation sites to coordinate with Zn²⁺, thereby minimizing water molecules within Zn-ion solvation sheaths, and greatly inhibit water-induced side-reactions and HER. Moreover, the N-ac chelating additive can form a unique physical barrier interface on Zn surface, preventing the harmful contacting with water. In addition, the preferential adsorption of N-ac on Zn (002) facets can promote highly reversible and dendrite-free Zn²⁺ deposition. As a result, Zn//Cu half-cell within N-ac added electrolyte delivered ultra-high 99.89 % Coulombic efficiency during 8000 cycles. Zn//Zn symmetric cells also demonstrated unprecedented long life of more than 9800 hours (over one year). Aqueous Zn//ZnV₆O₁₆ ⋅ 8H₂O (Zn//ZVO) full-cell preserved 78 % capacity even after ultra-long 2000 cycles. A more practical pouch-cell was also obtained (90.2 % capacity after 100 cycles). This method offers a promising strategy for accelerating the development of highly efficient AZMBs.