Strength Characteristics, Ultrasonic Wave Velocity, and the Correlation between Them in Clay Bricks under Dry and...

One of the methods used to discover the development of deterioration in bricks used as a construction material in a building is the monitoring of the bricks' strength characteristics over time. However, measuring the strength characteristics of bricks used in a building requires sampling for performing laboratory tests, which is not possible in some cases. As an alternative, ultrasonic wave velocity can be a useful, nondestructive tool for the indirect assessment of the strength characteristics of the bricks. In the present study, six different samples of clay bricks before utilization as construction materials in buildings located in Khorramabad City (Lorestan Province, western Iran) were collected. The mineralogical composition of the samples was studied using X-ray diffraction (XRD) analysis. As one common physical characteristic of the construction materials, the porosity (n) of the samples was measured. Next, the strength characteristics, including uniaxial compressive strength (UCS), Brazilian tensile strength (BTS), and P-wave velocity (Vp), of the samples under dry and saturated conditions were determined. It was found that after the saturation of the samples, considerable decreases in the UCS and BTS and increases in the Vp occurred, respectively. By comparing the values of the UCS, BTS, and Vp of the samples under dry and saturated conditions, we found that the integrity loss for the UCS and BTS was higher than for the Vp. Results showed that the integrity loss of the UCS, BTS, and Vp was significantly affected by the n and clay mineral (CM) content of the samples. Considering the dry or saturated condition of the samples, there are good correlations with acceptable accuracy levels between the Vp and the UCS and BTS, with coefficients of determination (R²) varying from 0.95 to 0.98. Consequently, our findings showed that establishing UCS and BTS predictive equations for bricks before their use as a construction material can be a worthy, practical tool for monitoring the deterioration of bricks over time after their utilization in a building.