The Inhibition Action of Some Brij-Type Nonionic Surfactants on the Corrosion of OLC 45 in Various Aggressive...

The corrosion protection property of three Brij-type surfactants, namely, Brij 35, Brij 56 and Brij 58P, was considered on OLC 45 carbon steel in a 0.5 M H₂SO₄ medium. The efficacy for these organic compounds was examined using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) methods, scanning electron microscopy (SEM) procedures, and Fourier transform infrared (FT-IR) spectroscopy. We hypothesized that these surfactants hinder the corrosion for OLC 45 samples through a protecting mechanism owing to the adsorption of organic molecules that form an inhibitive film or through the formation of complex oxides. These surfactants exhibited an appreciable protective effect against OLC 45 corrosion, operating as mixed inhibitors, as could be demonstrated by their influence on the electrochemical characteristics of the metallic substrates. The adsorption of surfactants over the substrates zone conformed to the representation of the Langmuir isotherm. The effect of temperature on the electrochemical comportment of the OLC 45 specimens in H₂SO₄ without and with Brij at 800 ppm was examined in the temperature interval of 293 to 333 K. The negative estimate of thermodynamic attributed as Gibbs free energy of adsorption presented the spontaneity of the adsorption activity. The investigation with FT-IR and SEM established the adsorption of Brij and the constitution of the corrosive components on the OLC 45 surface. Electrochemical determinations of these surfactants indicated its anticorrosion inhibition performance and the highest inhibition of 96% was reached when the Brij 35 concentration was at 800 or 1000 ppm, while for Brij 56 and Brij 58P, the highest inhibition was obtained when their concentrations were 500, 800, or 1000 ppm.