Analysis of Selected Properties of Polymer Mixtures Derived from Virgin and Re-Granulated PP with Glass Fibers

The problem of the growing amount of waste polymer materials currently affects virtually every area of the global economy. New actions taken by the E.U. and member states could lead to a reduction in the burden on the natural environment, as well as the reuse of thermoplastic waste. The aim of this study was to analyze the possibility of reusing post-industrial waste (recycled polypropylene-rPP) in order to produce mixtures with original polypropylene (PP) and glass fibers. The research undertaken is characterized by a high level of innovation and was carried out on an industrial scale from industrial waste. The primary goal of the analyses was to determine changes in the properties of the polymer mixtures depending on the amount of recycled polymers. For this purpose, four types of mixtures were prepared, characterized by different degrees of filling with recycled material obtained from big-bag packaging (the filling levels were 0 wt.%, 20 wt.%, 30 wt.%, and 70 wt.%). A detailed analysis of the physical properties of the obtained mixtures was carried out to determine changes in the densities depending on the amount of rPP material. In addition, changes in the MFIs (melt flow indexes), characterizing viscosity changes, were analyzed depending on the amount of secondary raw material used. An analysis of the mechanical properties was also carried out based on static tensile testing, the impact strength (the Charpy method), and the Rockwell hardness test (the M method). The analysis of the thermal changes was performed using the DSC method. The results showed that the composites made of virgin polypropylene (PP GF30) and those made from re-granulates and glass fibers (rPP GF30) are characterized by similar mechanical properties and significantly different processing properties, determined by MFI. This means that the addition of re-granulates significantly affects the processability of the obtained materials, while the addition of glass fibers maintains the basic mechanical properties.