Influence of Graphene Oxide on Mechanical Properties and Durability of Cement Mortar

The effect of graphene oxide (GO) on the mechanical strengths and durability of cement composites was researched by preparing GO-modified cement mortars. Thermogravimetric analysis (TGA) and nuclear magnetic resonance (²⁹Si MAS-NMR) were performed on the cement paste to evaluate the influence of GO on the hydration process and chain structure of calcium-silicate-hydrate (C-S-H) gels. TGA revealed that the high GO dosage increased the content of C-S-H by 5.46% compared with the control at 28 days. Similarly, ²⁹Si-NMR improved the hydration degree and main chain length (MCL) in GO-modified samples at 28 days. The GO led to increases of 2.54% and 7.01% in the hydration degree and MCL, respectively, compared with the control at 28 days. These findings underscore the multifaceted role of GO in improving the mechanical properties and durability of cement composites. Mechanical strength tests, such as compressive and flexural tests, were conducted on cement mortars. The optimal dosage of GO increased the compressive strength by 9.02% after 28 days. Furthermore, the flexural strength of cement mortars with the combination of GO and superplasticizer (SP) after 28 days increased by 21.86%, compared with reference mortar. The impact of GO proved to be more pronounced and beneficial in the durability tests, suggesting that GO can enhance the microstructure through hydration products to create a dense and interconnected microstructure.