Micron-Sized Thiol-Functional Polysilsesquioxane Microspheres with Open and Interconnected Macropores: Preparation,...

Polysilsesquioxane (PSQ) microspheres have shown promise in many fields, but previous studies about porous PSQ microspheres are scarce. Herein, we fabricated novel micron-sized thiol-functional polysilsesquioxane (TMPSQ) microspheres with open and interconnected macropores by combining inverse suspension polymerization with two-step sol-gel and polymerization-induced phase separation processes, without using phase-separation-promoting additives or sacrificial templates. The chemical composition of the TMPSQ microspheres was confirmed using FTIR and Raman spectroscopy. The morphology of the TMPSQ microspheres was characterized using SEM and TEM. TGA was employed to test the thermal stability of the TMPSQ microspheres. Mercury intrusion porosimetry and nitrogen adsorption-desorption tests were performed to investigate the pore structure of the TMPSQ microspheres. The results showed that the TMPSQ microspheres had open and interconnected macropores with a pore size of 839 nm, and the total porosity and intraparticle porosity reached 70.54% and 43.21%, respectively. The mechanism of porous generation was proposed based on the morphological evolution observed using optical microscopy. The macropores were formed through the following four steps: phase separation (spinodal decomposition), coarsening, gelation, and evaporation of the solvent. The macropores can facilitate the rapid mass transfer between the outer and inner spaces of the TMPSQ microspheres. The TMPSQ microspheres are promising in various fields, such as catalyst supports and adsorbents.