Facile Preparation of Cellulose Beads with Tunable Graded Pores and High Mechanical Strength

Cellulose-based hierarchical porous beads exhibit significant application potential in adsorption and separation systems due to their degradation and biocompatibility. However, the current fabrications of cellulose beads show poor mechanical properties and a difficult-to-regulate hierarchical porous structure, reducing their lifespan of use and limiting their application in fine separation. Here, we reported the facile creep-drop method to prepare cellulose beads that enabled systemic regulation of the macro-size, micropore structures, and mechanical properties by optimizing injection nozzle diameter, the composition of the coagulation bath, the temperature of the coagulation bath, and cellulose concentration. Notably, during the molding process, the H₂SO₄-Na₂SO₄ composite solidification bath endowed cellulose beads with a dense shell layer and a loose core layer, which achieved the integration of mechanical properties and high porosity. The cellulose beads exhibited high porosity (93.38-96.18%) and high sphericity (86.78-94.44%) by modulating the shell thickness of the cellulose beads. In particular, the cellulose beads exhibited excellent mechanical properties with a high compressive strength of 544.24 kPa at a 5% cellulose concentration. It is expected that these cellulose beads with tunable microstructures can realize their potential for applications in the fields of wastewater treatment, chemical engineering, bioengineering, medicine, and pharmaceuticals.