Surface Treatment Effect on the Mechanical and Thermal Behavior of the Glass Fabric Reinforced Polysulfone

The chemical structure of the surface of glass fibers, including silanized fibers, was studied. Highly efficient heat-resistant composites were obtained by impregnating silanized glass fiber with a polysulfone solution, and the effect of modification of the surface of glass fibers on the physical, mechanical and thermophysical properties of the composite materials was studied. As a result of the study, it was found that the fiber-to-polymer ratio of 70/30 wt.% showed the best mechanical properties for composites reinforced with pre-heat-treated and silanized glass fibers. It has been established that the chemical treatment of the glass fibers with silanes makes it possible to increase the mechanical properties by 1.5 times compared to composites reinforced with initial fibers. It was found that the use of silane coupling agents made it possible to increase the thermal stability of the composites. Mechanisms that improve the interfacial interaction between the glass fibers and the polymer matrix have been identified. It has been shown that an increase in adhesion occurs both due to the uniform distribution of the polymer on the surface of the glass fibers and due to the improved wettability of the fibers by the polymer. An interpenetrating network was formed in the interfacial region, providing a chemical bond between the functional groups on the surface of the glass fiber and the polymer matrix, which was formed as a result of treating the glass fiber surface with silanes, It has been shown that when treated with aminopropyltriethoxysilane, significant functional unprotonated amino groups NH⁺/NH₂⁺ are formed on the surface of the fibers; such free amino groups, oriented in the direction from the fiber surface, form strong bonds with the matrix polymer. Based on experimental data, the chemical structure of the polymer/glass fiber interface was identified.