Two-Dimensional Metal Halide Perovskites Created by Binary Conjugated Organic Cations for High-Performance Perovskite...

Studies indicated that two-dimensional (2D) metal halide perovskites (MHPs) embodied with three-dimensional (3D) MHPs were a facile way to realize efficient and stable perovskite solar cells (PSCs) and perovskite photodetectors (PPDs). Here, high-performance PSCs and PPDs, which are based on 2D/3D MHPs bilayer thin films, where the 2D MHPs are created by binary conjugated organic cations, are reported. Systemically studies reveal that the above novel 2D/3D MHPs bilayer thin films possess an enlarged crystal size, balanced charge transport, reduced charge carrier recombination, smaller charge-transfer resistance, and accelerated charge-extraction process compared to the 2D/3D MHPs bilayer thin films, where the 2D MHPs are created by a single conjugated organic cation. As a result, the PSCs based on the above novel 2D/3D MHPs bilayer thin film exhibit a power conversion efficiency of 22.76%. Moreover, unencapsulated PSCs possess dramatically enhanced stability compared with those based on the 2D/3D MHPs bilayer thin films, where the 2D MHPs are created by a single conjugated organic cation. In addition, the PPDs based on the above novel 2D/3D MHPs bilayer thin film exhibit a projected detectivity of 10¹⁶ cm Hz^1/2/W and a linear dynamic range of 108 dB at room temperature. Our studies indicate that the development of binary conjugated organic cation-based 2D MHPs incorporated with 3D MHPs is a simple method to realize high-performance PSCs and PPDs.