Zinc-Ion Anchor Induced Highly Reversible Zn Anodes for High Performance Zn-Ion Batteries

Unstable Zn interface with serious detrimental parasitic side-reactions and uncontrollable Zn dendrites severely plagues the practical application of aqueous zinc-ion batteries. The interface stability was closely related to the electrolyte configuration and Zn²⁺ depositional behavior. In this work, a unique Zn-ion anchoring strategy is originally proposed to manipulate the coordination structure of solvated Zn-ions and guide the Zn-ion depositional behavior. Specifically, the amphoteric charged ion additives (denoted as DM), which act as zinc-ion anchors, can tightly absorb on the Zn surface to guide the uniform zinc-ion distribution by using its positively charged -NR₄ ⁺ groups. While the negatively charged -SO₃ ^- groups of DM on the other hand, reduces the active water molecules within solvation sheaths of Zn-ions. Benefiting from the special synergistic effect, Zn metal exhibits highly ordered and compact (002) Zn deposition and negligible side-reactions. As a result, the advanced Zn||Zn symmetric cell delivers extraordinarily 7000 hours long lifespan (0.25 mA cm^-2, 0.25 mAh cm^-2). Additionally, based on this strategy, the NH₄V₄O₁₀||Zn pouch-cell with low negative/positive capacity ratio (N/P ratio=2.98) maintains 80.4 % capacity retention for 180 cycles. A more practical 4 cm*4 cm sized pouch-cell could be steadily cycled in a high output capacity of 37.0 mAh over 50 cycles.