Minoxidil Nanosuspension-Loaded Dissolved Microneedles for Hair Regrowth

Minoxidil (MIN) is used topically to treat alopecia. However, its low absorption limits its use, warranting a new strategy to enhance its delivery into skin layers. The objective of this study was to evaluate the dermal delivery of MIN by utilizing dissolved microneedles (MNs) loaded with MIN nanosuspension (MIN-NS) for hair regrowth. MIN-NS was prepared by the solvent-antisolvent precipitation technique. The particle size of MIN-NS was 226.7 ± 9.3 nm with a polydispersity index of 0.29 ± 0.17 and a zeta potential of -29.97 ± 1.23 mV. An optimized formulation of MIN-NS was selected, freeze-dried, and loaded into MNs fabricated with sodium carboxymethyl cellulose (Na CMC) polymeric solutions (MIN-NS-loaded MNs). MNs were evaluated for morphology, dissolution rate, skin insertion, drug content, mechanical properties, ex vivo permeation, in vivo, and stability studies. MNs, prepared with 14% Na CMC, were able to withstand a compression force of 32 N for 30 s, penetrate Parafilm M® sheet at a depth of 374-504 µm, and dissolve completely in the skin within 30 min with MIN %recovery of 95.1 ± 6.5%. The release of MIN from MIN-NS-loaded MNs was controlled for 24 h. MIN-NS-loaded MNs were able to maintain their mechanical properties and chemical stability for 4 weeks, when kept at different storage conditions. The in vivo study of the freeze-dried MIN-NS and MIN-NS-loaded MNs proved hair regrowth on rat skin after 11 and 7 days, respectively. These results showed that MIN-NS-loaded MNs could potentially improve the dermal delivery of MIN through the skin to treat alopecia.