Hydrothermal Synthesis of Cancrinite from Coal Gangue for the Immobilization of Sr

The primary objective of this study is to investigate and develop a rapid and effective method for the immobilization of Sr in the event of a nuclear leakage incident. Coal gangue, an underutilized form of solid waste from the coal industry, can be used as a raw material for curing Sr due to its high content of silica-alumina oxides. In the present study, Sr was successfully solidified in cancrinite synthesized using a hydrothermal method with coal gangue as raw material. A stable cancrinite phase was formed at a relative alkali concentration of more than 6 M. When the Sr/Al(Si) ratio was <1/6, cancrinite was the only stable phase that varied with the hydrothermal temperature and time. When the Sr/Al(Si) ratio increased to 1/2, the cancrinite phase completely disappeared, and a new strontium feldspar phase (SrAl₂Si₂O₈) appeared. PCT leaching experiments showed that when Sr/Al(Si) < 1/6, the Sr leaching rate of Sr-cancrinite samples obtained by hydrothermal synthesis at 180 °C for 24 h was very low.