An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature
Published on: September 23, 2018
Optimizing the Strength and Toughness of V/Mo-Modified 0.22C-5.24Mn Steel by Short-Time Partial Austenitization
Haoqing Zheng1, Gang Liu2,3, Shuai Tong2
1State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Pangang Group, Panzhihua 617000, China.
Abstract:
In order to obtain the good match between yield strength and low-temperature toughness, the short-time partial austenitization (SPA) process was employed for V/Mo-bearing 0.22C-5.24Mn steel. The initial microstructure after intercritical tempering was dual-phase ferrite and reversed austenite (RA), while the final microstructure consisted of ferrite, RA, and secondary martensite (SM) after being subjected to the SPA process. (V, Mo)C with disclike morphology mainly precipitated during intercritical tempering, and the aspect ratio of particles decreased, leading to the appearance of near-spherical morphology. After being subjected to SPA process, the resultant multiphase hierarchical microstructure (three layers: outer layer of ferrite, interlayer of SM, and inner layer of RA) enabled a high yield strength of 1097 MPa, a total elongation of 14%, and an impressive impact energy of 33.3 J at -20 °C. The strengthening contribution of (V, Mo)C precipitation was estimated to be about 108 MPa.
Related Concept Videos
01:18Mechanical Characteristics of Steel
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
01:26Steel Manufacturing
During this smelting process, limestone plays a crucial role by forming slag. Slag captures impurities within the molten iron, such...
01:15Posttensioned Masonry Walls
Post-tensioned masonry walls use high-strength steel rods or flexible tendons to enhance the strength and efficiency of masonry structures. These elements are securely anchored to the foundation and extend vertically either within the cores of the masonry units or between the masonry wythes. The construction process involves building the wall with these tensioning elements in place and allowing the mortar to fully cure.
Following the curing process, the tensioning begins. Steel rods are...
01:29Strength and Heat of Hydration
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
01:17Steel Fastening Techniques
Rivets are cylindrical steel fasteners with a specially designed head. During application, rivets are heated until white-hot and then inserted through pre-drilled holes in the steel sections. A pneumatic hammer is used to shape the exposed end into a second head, securing the sections together.
Bolting is another...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...