Manipulating the ionic conductivity and interfacial compatibility of polymer-in-dual-salt electrolytes enables
Wentao Lin1, Dengjie Chen2, Jing Yu3
1College of Chemistry and Chemical Engineering, Zhongkai University of Agriculture and Engineering, Guangzhou 510225, China; College of Chemistry and Materials Science, Guangdong Provincial Key Laboratory of Functional Supramolecular Coordination Materials and Applications, Guangdong Engineering & Technology Research Centre of Graphene-Like Materials and Products, Jinan University, Guangzhou 510632, China.
Abstract:
Solid polymer electrolytes (SPEs) have shown great promise in the development of lithium-metal batteries (LMBs), but SPEs' interfacial instability and limited ionic conductivity still prevent their widespread applications. Herein, high-concentration hybrid dual-salt "polymer-in-salt" electrolytes (HDPEs) through formulation optimization were facilely prepared to simultaneously boost ionic conductivity, improve interfacial compatibility, and ensure a wide-temperature-range operation with high safety. An optimized electrolyte (HDPE-0.6) shows negligible corrosion to the aluminum current collector after manipulating the salt ratio of lithium bis(trifluoromethane)sulfonimide and lithium bis(oxalato)borate. In addition, HDPE-0.6 has excellent ionic conductivity (i.e., ∼0.536, ∼0.898, and ∼1.28 mS cm-1 at 0, 30, and 60 °C), approaching 1 mS cm-1 at room temperature. Furthermore, HDPE-0.6 exhibits a high lithium transference number of 0.6 and a high electrochemical oxidation stability potential of > 4.8 V vs. Li/Li+. Additionally, due to the formulation of high-concentration thermally stable lithium salts and the employment of flame-retardant trimethyl phosphate as the solvent, HDPE-0.6 has no safety issues. The resultant LiFePO4|HDPE-0.6|Li cell exhibits high discharge capacity, good rate capability, and excellent cycle stability at extended temperatures of 0, 30, and 60 °C. By coupling theoretical calculations and in-depth X-ray photoelectron spectroscopy, we attribute the excellent cycle stability to the formation of a stable interphase. Moreover, our formulation strategy is suitable for the Na3V2(PO4)3//Na battery when replacing the lithium salts with sodium salts (i.e., sodium bis(trifluoromethane)sulfonimide and sodium bis(oxalato)borate) to yield HDPE-0.6-Na, as demonstrated by excellent cycle stability (e.g., 98.6 % of capacity retention after 300 cycles). Our work demonstrates that the as-developed quasi-solid HDPEs are suitable for LMBs and sodium-metal batteries, and HDPEs can function normally in a wide temperature range.