Research on Coated Tool Life and Wear in Ta-2.5W Alloy Turning

Bo Hu1, Zhengqing Liu1, Yang Wu2

  • 1College of Mechanical Engineering, Zhejiang University of Technology, Hangzhou 310023, China.

Materials (Basel, Switzerland)
|April 13, 2024
PubMed

Keywords:
Ta-2.5W alloycoated toolcutting temperaturetool lifetool wearturning

More Related Videos

Experimental Procedure for Warm Spinning of Cast Aluminum Components07:36

Experimental Procedure for Warm Spinning of Cast Aluminum Components

Published on: February 1, 2017

9.5K
Knowledge Based Cloud FE Simulation of Sheet Metal Forming Processes11:05

Knowledge Based Cloud FE Simulation of Sheet Metal Forming Processes

Published on: December 13, 2016

12.2K

Related Concept Videos

Screw: Problem Solving01:21

Screw: Problem Solving

In mechanical engineering, the interaction between a threaded screw shaft and a plate gear involves analyzing the resisting torque on the plate gear that can be overpowered when a specific torsional moment is applied to the shaft. To better comprehend this concept, consider a generic situation with a threaded screw shaft with a given mean radius and lead and a plate gear with a specified mean radius. The coefficient of static friction between the screw and gear is also provided.
To evaluate the...
415
Thin-Walled Hollow Shafts01:15

Thin-Walled Hollow Shafts

In analyzing a thin-walled hollow shaft subjected to torsional loading, a segment with width dx is isolated for examination. Despite its equilibrium state, this segment faces torsional shearing forces at its ends. These forces are quantitatively described by the product of the longitudinal shearing stress on the segment's minor surface and the area of this surface, leading to the concept of shear flow. This shear flow is consistent throughout the structure, indicating a uniform distribution...
186
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
130
Design Example: Deciding Thickness of Lubricating Fluid in a Shaft01:23

Design Example: Deciding Thickness of Lubricating Fluid in a Shaft

Effective lubrication between a rotating shaft and its bearing housing is essential in rotating machinery to minimize friction, wear, and energy loss. With carefully controlled thickness and viscosity, the lubricant layer prevents metal-to-metal contact, ensuring smooth operation.
To calculate the required thickness of the lubricant layer, the tangential velocity at the shaft's surface must first be determined. This velocity is calculated by converting the rotational speed to angular...
109
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
181
Residual Stresses in Circular Shafts01:10

Residual Stresses in Circular Shafts

In materials that exhibit elastic and plastic behavior, known as elastoplastic materials, residual stresses can accumulate when these materials experience plastic deformation. This deformation arises from either high levels of shearing stress or significant strains. Residual stresses are internal stresses that persist within a material after removing the external force causing deformation. This phenomenon is demonstrated when observing the behavior of a shaft under torque; notably, the...
170