Synthesis of guar gum maleate under dry conditions: Reaction kinetics and characterization

In the present study, a novel environment friendly dry method for preparation of guar gum maleate (GGM) with varying degrees of substitution (DS; 0.02-1.04) was optimized. GGM with a maximum DS of 1.04 was successfully synthesized using guar gum (GG) and maleic anhydride (MA) in proportion of 1: 1 at 80 °C with 4 h of reaction time. The activation energy for the reaction was determined to be 36.91 ± 3.61 kJ mol^-1 with pre-exponential factor of 1392 min^-1. Esterification of GG was confirmed by FT-IR and ¹³C NMR. Analysis using size exclusion chromatography (SEC) indicated a decrease in weight average molecular weight (M_w) of the polymer with an increase in polydispersity index (PDI) due to esterification. In comparison with GG, GGM displayed increased hydrophobicity and reduced thermal stability, as analysed by differential scanning calorimetry (DSC). Rheological studies of GGM revealed that initial apparent viscosity decreased with increasing DS. For the first time, the study offered valuable insights on GGM synthesis under dry solvent-less reaction conditions enabling simpler and scalable synthesis process.