Influence of Varied Silane Commercial Brands and Adhesive Application on Bond Strength and Stability to Lithium
E T Calixto1, V F Kelmer2, G H Komegae3
1Emerson Tavares Calixto, DDS, MSc student, Ingá University Center, Uningá, Maningá, PR, Brazil.
Objectives:
This study aimed to evaluate the impact of various commercial silane brands with varied chemical compositions with or without the application of an adhesive layer on the microshear bond strength and durability of a resin luting agent to lithium disilicate glass ceramic.
Methods And Materials:
Lithium disilicate glass ceramic discs (EMX, IPS e.max Press, Ivoclar Vivadent) measuring 10 mm in diameter and 3 mm in thickness were fabricated (n=240). Surfaces were etched using 5% hydrofluoric acid and randomly assigned to 10 groups based on the commercial brand of silane used (n=24): [RP] RelyX Ceramic Primer (3M ESPE); [PS] Prosil (FGM); [SA] Silano (Angelus); [SM] Silano (Maquira); [SU] Silane (Ultradent); [GL] GLUMA Ceramic Primer (Kulzer); [CB] Ceramic Bond (VOCO); [MB] Monobond N (Ivoclar Vivadent); [CP] Clearfil Ceramic Primer (Kuraray); and [DE] 2-step silane (Dentsply Sirona). Half of the EMXs (n=12) received a thin adhesive layer (+) after the silane and prior to resin luting agent, while the other half (n=12) did not receive an adhesive layer (-). For the microshear bond strength test (μSBS), four light-cured resin luting agent cylinders (1 mm in diameter) were created on each EMX surface. Half of these specimens were tested after 24 hours, while the other half were stored in deionized water for 6 months. The μSBS test was conducted using a universal testing machine (DL 500, EMIC) at a crosshead speed of 1 mm/min until failure. The obtained data underwent statistical analysis using analysis of variance (ANOVA) and the Tukey test (α=0.05).
Results:
There was significant influence of the silane commercial brand on bond strength. Notably, "universal primers" yielded lower bond strength results compared to "pure" silane solutions. Water storage had a detrimental effect on microshear bond strength for certain silane commercial brands. Additionally, the application of an adhesive layer negatively impacted bond strength results for all silanes.
Conclusions:
This study confirms the importance of both silane commercial brand and chemical composition in relation to bond strength of resin luting agents to lithium disilicate glass ceramic. Furthermore, the application of an adhesive layer may have an adverse effect on bond stability over time.