Structure and Properties of Epoxy Resin/Graphene Oxide Composites Prepared from Silicon Dioxide-Modified Graphene...

In this study, graphene oxide (GO) was modified via electrostatic interactions and chemical grafting by silica (SiO₂), and two SiO₂@GO hybrids (GO-A and GO-B, respectively) with different structures were obtained and carefully characterized. Results confirmed the successful grafting of SiO₂ onto the GO surface using both strategies. The distribution of SiO₂ particles on the surface of GO-A was denser and more agglomerated, while it was more uniform on the surface of GO-B. Then, epoxy resin (EP)/GO composites were prepared. The curing mechanism of EP/GO composites was studied by differential scanning calorimetry and in situ infrared spectra spectroscopy. Results of tensile tests, hardness tests, dynamic mechanical analysis, and dielectric measurement revealed that EP/GO-B exhibited the highest tensile properties, with a tensile strength of 79 MPa, a 43% increase compared to raw EP. Furthermore, the addition of fillers improved the hardness of EP, and EP/GO-B showed the highest energy storage modulus of 1900 MPa. The inclusion of SiO₂@GO hybrid fillers enhanced the dielectric constant, volume resistivity, and breakdown voltage of EP/GO composites. Among these, EP/GO-B displayed the lowest dielectric loss, relatively good insulation, and relatively high volume resistivity and breakdown voltage. A related mechanism was proposed.