3D Printing Silk Fibroin/Polyacrylamide Triple-Network Composite Hydrogels with Stretchability, Conductivity, and...

Electronic skins have received increasing attention due to their great application potential in wearable electronics. Meanwhile, tremendous efforts are still needed for the fabrication of multifunctional composite hydrogels with complex structures for electronic skins via simple methods. In this work, a novel three-dimensional (3D) printing composite hydrogel with stretchability, conductivity, and strain-sensing ability is produced using a one-step photocuring method to achieve a dual-signal response of the electronic skin. The composite hydrogel exhibits a triple-network structure composed of silk microfibers (SMF), regenerated silk fibroin (RSF), and polyacrylamide (PAM). The establishment of triple networks is based on the electrostatic interaction between SMF and RSF, as well as the chemically cross-linked RSF and PAM. Thanks to its specific structure and components, the composite hydrogel possesses enhanced mechanical properties (elastic modulus of 140 kPa, compressive stress of 21 MPa, and compression modulus of 600 kPa) and 3D printability while retaining stretchability and flexibility. The interaction between negatively charged SMF and cations in phosphate-buffered saline endows the composite hydrogel with good conductivity and strain-sensing ability after immersion in a low-concentration (10 mM) salt solution. Moreover, the 3D printing composite hydrogel scaffold successfully realizes real-time monitoring. Therefore, the proposed hydrogel-based ionic sensor is promising for skin tissue engineering, real-time monitoring, soft robotics, and human-machine interfaces.