Preparation and Characterization of Bismaleimide-Resin-Based Composite Materials

This study utilized bismaleimide (BMI) resin, reinforced with introduced ether bonds, as a binding matrix, in combination with silicon carbide (SiC), for the fabrication of composite materials. A thorough investigation was conducted to assess the influence of diverse processing parameters on the mechanical properties and high-temperature thermo-oxidative stability of these composites. Experimental results indicate a notable improvement in the mechanical properties of the composites upon the incorporation of ether bonds, in contrast to their unmodified counterparts. The variation in performance among composites with different ratios and molding densities is apparent. Within a certain range, an increase in resin content and molding density is correlated with improved bending strength in the composites. With a resin content of 27.5 vol% and a molding density of 2.31 g/cm³, the composite achieved a maximum flexural strength of 109.52 MPa, representing a 24% increase compared to its pre-modification state. Even after exposure to high-temperature heat treatment, the composites displayed commendable mechanical properties compared to their pre-ether bond modification counterparts, maintaining 74.5% of the strength of the untreated composites at 300 °C. The scanning electron microscopy (SEM) microstructures of composite materials correlate remarkably well with their mechanical properties.