Microstructure Evolution and Fretting Wear Mechanisms of Steels Undergoing Oscillatory Sliding Contact in Dry...

Variations in the microstructure and the dominant fretting wear mechanisms of carbon steel alloy in oscillatory sliding contact against stainless steel in a dry atmosphere were evaluated by various mechanical testing and microanalytical methods. These included scanning electron microscopy and energy dispersive spectrometry with corresponding elemental maps of the wear tracks, in conjunction with cross-sectional transmission electron microscopy of samples prepared by focused ion beam machining to assess subsurface and through-thickness changes in microstructure, all as a function of applied load and sliding time. Heavily dislocated layered microstructures were observed below the wear tracks to vary with both the load and sliding time. During the accumulation of fretting cycles, the subsurface microstructure evolved into stable dislocation cells with cell walls aligned parallel to the surface and the sliding direction. The thickness of the damaged subsurface region increased with the load, consistent with the depth distribution of the maximum shear stress. The primary surface oxide evolved as Fe₂O₃ and Fe₃O₄ with increasing sliding time, leading to the formation of a uniform oxide scale at the sliding surface. It is possible that the development of the dislocation cell structure in the subsurface also enhanced oxidation by pipe diffusion along dislocation cores. The results of this study reveal complex phase changes affecting the wear resistance of steels undergoing fretting wear, which involve a synergy between oxidative wear, crack initiation, and crack growth along dislocation cell walls due to the high strains accumulating under high loads and/or prolonged surface sliding.