Statistical simplex centroid experimental design for evaluation of pectin, modified chitosan and modified starch as...

Vitamin E encapsulation into biopolymer-based microparticles, obtained by spray-drying technology, was proposed to improve the encapsulation efficiency and the controlled release of fat-soluble vitamin. Binary and ternary blends of pectin, modified chitosan and modified starch, modified starch + modified chitosan, modified starch + pectin, modified chitosan + pectin and modified starch + modified chitosan + pectin ((0.33, 0.33, 0.33), (0.70, 0.15, 0.15), (0.15, 0.70, 0.15) and (0.15, 0.15, 0.70)) were proposed to produce and evaluate different carrier-based delivery systems. Vitamin E-loaded microparticles and empty microparticles were created with a product yield between 9 and 49 %. The mean diameter among all microparticles varied between 3.74 ± 0.02 and 421 ± 21 μm (differential volume distribution). Oval, spherical or irregular microparticles, with a variable morphology from a smooth to a high rough surface structure, with concavities, were produced. All vitamin E-loaded microparticles exhibited an encapsulation efficiency higher than 70 %. The slower vitamin E controlled release was observed from microparticles composed by modified chitosan (>36 h), while the faster release was achieved from microparticles individually composed by pectin (39 min). In general, the Fickian diffusion is the main release mechanism involved in the microparticles produced with modified chitosan, other formulations combine also other mechanisms such as swelling.