Improvement of Photovoltaic Performance of Perovskite Solar Cells by Synergistic Modulation of SnO₂ and Perovskite...

In the past decade, perovskite solar cell (PSC) photoelectric conversion efficiency has advanced significantly, and tin dioxide (SnO₂) has been extensively used as the electron transport layer (ETL). Due to its high electron mobility, strong chemical stability, energy level matching with perovskite, and easy low-temperature fabrication, SnO₂ is one of the most effective ETL materials. However, the SnO₂ material as an ETL has its limitations. For example, SnO₂ films prepared by low-temperature spin-coating contain a large number of oxygen vacancies, resulting in energy loss and high open-circuit voltage (V_OC) loss. In addition, the crystal quality of perovskites is closely related to the substrate, and the disordered crystal orientation will lead to ion migration, resulting in a large number of uncoordinated Pb²⁺ defects. Therefore, interface optimization is essential to improve the efficiency and stability of the PSC. In this work, 2-(5-chloro-2-benzotriazolyl)-6-tert-butyl-p-cresol (CBTBC) was introduced for ETL modification. On the one hand, the hydroxyl group of CBTBC forms a Lewis mixture with the Sn atom, which reduces the oxygen vacancy defect and prevents nonradiative recombination. On the other hand, the SnO₂/CBTBC interface can effectively improve the crystal orientation of perovskite by influencing the crystallization kinetics of perovskite, and the nitrogen element in CBTBC can effectively passivate the uncoordinated Pb²⁺ defects at the SnO₂/perovskite interface. Finally, the prevailing PCE of PSC (1.68 eV) modified by CBTBC was 20.34% (V_OC = 1.214 V, J_SC = 20.49 mA/cm², FF = 82.49%).