Fracture resistance and failure mode of three esthetic CAD-CAM post and core restorations
Islam T Fathey1, Amir Shoukry Azer2, Islam M Abdelraheem2
1Division of Fixed Prosthodontics, Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, P. O. Box: 21527, Champollion St., Azarita, Alexandria, Egypt. islam.fathey.dent@alexu.edu.eg.
Background:
The rising demand for improved aesthetics has driven the utilization of recently introduced aesthetic materials for creating custom post and core restorations. However, information regarding the fracture resistance of these materials remains unclear, which limits their practical use as custom post and core restorations in clinical applications. AIM OF THE STUDY: This study aimed to evaluate the fracture resistance of three non-metallic esthetic post and core restorations and their modes of failure.
Materials And Methods:
Thirty-nine single-rooted human maxillary central incisors were endodontically treated. A standardized post space preparation of 9mm length was performed to all teeth to receive custom-made post and core restorations. The prepared teeth were randomly allocated to receive a post and core restoration made of one of the following materials (n=13): glass fiber-reinforced composite (FRC), polyetheretherketone (PEEK) and polymer-infiltrated ceramic-network (PICN). An intraoral scanner was used to scan all teeth including the post spaces. Computer-aided design and computer-aided manufacturing (CAD-CAM) was used to fabricate post and core restorations. Post and core restorations were cemented using self-adhesive resin cement. All specimens were subjected to fracture resistance testing using a universal testing machine. Failure mode analysis was assessed using a stereomicroscope and SEM. The data was statistically analyzed using One-Way ANOVA test followed by multiple pairwise comparisons using Bonferroni adjusted significance level.
Results:
Custom PEEK post and core restorations displayed the least fracture load values at 286.16 ± 67.09 N. In contrast, FRC exhibited the highest average fracture load at 452.60 ± 105.90 N, closely followed by PICN at 426.76 ± 77.99 N. In terms of failure modes, 46.2% of specimens with PICN were deemed non-restorable, while for PEEK and FRC, these percentages were 58.8% and 61.5%, respectively.
Conclusions:
Within the limitation of this study, both FRC and PICN demonstrated good performance regarding fracture resistance, surpassing that of PEEK.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
03:02Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
Published on: January 17, 2025