Strong Local Polarization Fluctuations Enabled High Electrostatic Energy Storage in Pb-Free Relaxors

Electrostatic energy-storage ceramic capacitors are essential components of modern electrified power systems. However, improving their energy-storage density while maintaining high efficiency to facilitate cutting-edge miniaturized and integrated applications remains an ongoing challenge. Herein, we report a record-high energy-storage density of 20.3 J cm^-3 together with a high efficiency of 89.3% achieved by constructing a relaxor ferroelectric state with strongly enhanced local polarization fluctuations. This is realized by incorporating highly polarizable, heterovalent, and large-sized Zn and Nb ions into a Bi_0.5Na_0.5TiO₃-BaTiO₃ ferroelectric matrix with very strong tetragonal distortion. Element-specific local structure analysis revealed that the foreign ions strengthen the magnitude of the unit-cell polarization vectors while simultaneously reducing their orientation anisotropy and forming strong fluctuations in both magnitude and orientation within 1-3 nm polar clusters. This leads to a particularly high polarization variation (ΔP) of 72 μC cm^-2, low hysteresis, and a high effective polarization coefficient at a high breakdown strength of 80 kV mm^-1. This work has surpassed the current energy density limit of 20 J cm^-3 in bulk Pb-free ceramics and has demonstrated that controlling the local structure via the chemical composition design can open up new possibilities for exploring relaxors with high energy-storage performance.