Self-powered stable high-performance UV-Vis-NIR broadband photodetector based on PVP-Cobalt@Carbon nanofibers/n-GaAs
Roya Shokrani Havigh1, Fatma Yıldırım2, Hossein Mahmoudi Chenari1
1Department of Physics, Faculty of Science, University of Guilan, Namjoo Ave, PO Box 41335-1914, Rasht, Iran.
Abstract:
The self-powered PVP-Co@C nanofibers/n-GaAs heterojunction photodetector (HJPD) was fabricated by electrospinning of the nanofibers onto GaAs. An excellent rectification ratio of 6.60 × 106was obtained fromI-Vmeasurements of the device in the dark. TheI-Vmeasurements of the fabricated device under 365 nm, 395 nm and 850 nm lights, as well asI-Vmeasurements in visible light depending on the light intensity, were performed. The HJPD demonstrated excellent photodetection performance in terms of a good responsivity of ∼225 mA W-1(at -1.72 V) and at zero bias, an impressive detectivity of 6.28 × 1012Jones, and a high on/off ratio of 8.38 × 105, all at 365 nm wavelength. In addition, the maximum external quantum efficiency and NPDR values were 3495% (V = -1.72 V) and 2.60 × 1010W-1(V= 0.0 V), respectively, while the minimum NEP value was ∼10-14W.Hz-1/2for 365 nm atV= 0.V volts. The HJPD also exhibited good long-term stability in air after 30 d without any encapsulation.