Gradient Variation and Correlation Analysis of Physical and Mechanical Properties of Moso Bamboo (Phyllostachys...

This study aimed to investigate the gradient properties of bamboo at the microscopic level and provide a basis for improving the utilization rate of bamboo. Using moso bamboo (Phyllostachys edulis (Carrière) J. Houz.) as a research subject, the variation of vascular bundle area percentage, chemical content, relative crystallinity (CR), mechanical properties of different bamboo slivers, and correlation between those parameters were analyzed. From the bamboo green layer (BGL) to the bamboo yellow layer (BYL), the distribution of vascular bundles changed from dense to sparse. Cellulose and lignin mass content decreased gently, and hemicellulose mass content showed gradual increases. The CR showed an order of bamboo middle layer (BML) > BGL > BYL. The tensile modulus of elasticity, tensile strength, bending modulus of elasticity, and bending strength decreased from BGL to BYL. The order of influence degree on mechanical properties of moso bamboo was vascular bundle area, hemicellulose content, lignin mass content, density, and CR, and these factors correlated with mechanical properties at a significant level (p < 0.05). Vascular bundle area had a decisive effect on the mechanical properties of bamboo. The vascular bundle area and density were linearly correlated with mechanical properties, while the lignin mass content and CR were curve-linearly correlated with mechanical properties.