Management of ibuprofen in wastewater using electrospun nanofibers developed from PET and PS wastes

Electrospinning is a promising technique for the beneficial use and recycling of plastic waste polymers using simple methodologies. In this study, plastic bottles and Styrofoam wastes have been used to develop polyethylene terephthalate (PET) and polystyrene (PS) nanofibers using electrospinning technique separately without any further purification. The effect of the concentration onto the nanofiber's morphology was studied. The fabricated nanofibers were characterized using Field Emission Scanning Electron Microscope (FE-SEM), Fourier Transformed Infrared Spectroscopy (ATR-FTIR), N₂ adsorption/desorption analysis, and water contact angle (WCA). Furthermore, the prepared nanofibers were applied for the adsorption of ibuprofen (IBU) from wastewater. Some parameters that can influence the adsorption efficiency of nanofibers such as solution pH, wt.% of prepared nanofibers, drug initial concentration, and contact time were studied and optimized. The results show that the equilibrium adsorption capacity was achieved after only 10 min for 12 wt% PET nanofibers which is equivalent to 364.83 mg/g. For 12 wt% PS nanofibers, an equilibrium adsorption capacity of 328.42 mg/g was achieved in 30 min. The experimental data was fitted to five isotherm and four kinetics models to understand the complicated interaction between the nanofibers and the drug. Langmuir-Freundlich isotherm model showed the best fit for experimental data for both PET and PS nanofibers. The adsorption process was characterized by predominantly physical reaction rather than chemical adsorption for both materials. The reusability study revealed that the synthesized nanofibers maintain their ability to adsorb/desorb IBU for up to five cycles. The results obtained demonstrated that fabricated nanofibers from plastic wastes could perform promising adsorbents for the management of IBU in wastewater. However, further research is needed for the scaling-up the fabrication which is required for real-world applications.