Fabrication of Activated Carbon Derived from Glycerin Pitch for Desulfurization of Model Fuel Oil and Electrode...

One of the world's challenging energy issues is introducing practical and affordable technology for organosulfur removal in fuel. Adsorptive desulfurization (ADS) can address this issue if highly effective activated carbon (AC) derived from industrial waste with excellent textural properties is used. In this study, the derived ACs from glycerin pitch loaded with P and Fe (AC/P and AC/Fe) were used as adsorbents for the ADS of model fuel oils, such as dibenzothiophene (DBT) at mild operating conditions. Under the optimized experimental conditions, 0.3 g of adsorbent dosage, 60 min reaction time, 30 °C temperature, and pH 4, the maximal DBT removal of 96.28 and 43.64%, respectively, for AC/P and AC/Fe was realized. The results indicated that the phosphorus-doped AC/P increases the selectivity of the ADS mechanism for DBT removal. Kinetic investigations disclosed that the adsorption process follows second-pseudo-order kinetics and the Langmuir adsorption isotherm model. The adsorbents remained active for five successive reuses, indicating their robust real-world applications. The electrochemical properties of the fabricated carbon electrodes were analyzed via cyclic voltammetry by coating the ACs with polytetrafluoroethylene (PTFE) as a binder. The transition-metal-doped AC/Fe, though exhibiting 5 times lower surface area, showed the highest specific capacitance at a scan rate of 5 mVs^-1 (0.65 μF cm^-2). Similarly, the extended AC:PTFE capacitor at a 10% binder ratio offered the maximum capacitance value (1.13 μF cm^-2). The synthesized ACs demonstrated potential application as an electrode material, and hence glycerin pitch could be a low-cost precursor to improve the feasibility of commercial production of AC.