Improving Buried Interface Contact by Bidentate Anchoring for Inverted Perovskite Solar Cells

Nickel oxide (NiO_x) is a promising hole transport layer (HTL) to fabricate efficient and large-scale inverted perovskite solar cells (PSCs) due to its low cost and superior chemical stability. However, inverted PSCs based on NiO_x are still lagging behind that of other HTL because of the poor quality of buried interface contact. Herein, a bidentate ligand, 4,6-bis (diphenylphosphino) phenoxazine (2DPP), is used to regulate the NiO_x surface and perovskite buried interface. The diphosphine Lewis base in the 2DPP molecule can coordinate both with NiO_x and lead ions at NiO_x/perovskite interface, leading to high-quality perovskite films with minimized defects. It is found that the inverted PSCs with 2DPP-modified buried interface exhibit double advantages of being both fast charge extraction and reduced nonradiative recombination, which is a combination of multiple factors including favorable energetic alignment, improved interface contact and strong binding between NiO_x/2DPP and perovskite. The optimal PSC based on 2DPP modification yields a champion power conversion efficiency (PCE) of 21.9%. The unencapsulated PSC maintains above 75% of its initial PCE in the air with a relative humidity (RH) of 30-40% for 1000 h.