Eco-friendly multifunctional coating for polyester-cotton blended fabrics with superior flame retardancy and
Xiaoyun Zhang1, Ping Li1, Zhanna Liu1
1College of Textiles & Clothing, Institute of Functional Textiles and Advanced Materials, National Engineering Research Center for Advanced Fire-Safety Materials D & A (Shandong), Qingdao Key Laboratory of Flame Retardant Textile Materials, State Key Laboratory of Bio-Fibers and Eco-textiles, Qingdao University, Qingdao 266071, China.
Abstract:
Since the fire hazards of polyester-cotton blended (PTCO) fabrics and the hidden dangers of bacterial infection concerns caused by the contained cotton fiber, the design of flame retardant and antibacterial PTCO fabrics has received considerable attention. In this work, flame-retardant PTCO fabrics with satisfactory antibacterial properties were fabricated via a convenient and eco-friendly impregnation treatment involving guanidine phosphate (GP) and polyethylenimine (PEI). The prepared PTCO fabrics demonstrated excellent flame retardancy with a high limiting oxygen index value of 30.5 % and self-extinguishing capability, the damaged length was only 34 mm in the vertical flammability test. Furthermore, the peak heat release rate and the total heat release of coated PTCO fabrics were reduced significantly by 49 % and 38 %, respectively, indicating a substantial enhancement in fire safety. According to the analysis of the char residues and volatiles, GP presented great catalytic carbonization property, and PEI assisted the formation of the dense and stable carbon layer. The stable carbon layer effectively restricted mass and oxygen transfer between the PTCO fabrics and the environment. In addition, the introduction of PEI also produced more nonflammable gases to enhance the flame retardancy of the PTCO fabrics. Importantly, the GP/PEI coating barely deteriorate the physical and mechanical properties of the PTCO fabrics. The antibacterial rate of the GP/PEI-coated PTCO fabrics against Escherichia coli and Staphylococcus aureus was 99.99 %, similar to that of GP-coated fabrics, indicating the efficacy antibacterial properties of GP, and the addition of PEI did not compromise the antibacterial properties of GP. This work offers an efficient and simple approach to producing multifunctional PTCO fabrics with excellent flame retardancy and antibacterial properties, which are hopeful to expand the promising application of PTCO fabrics.