Synthesis of novel chitosan/sodium hyaluronate/iridium hydrogel nanocomposite for wound healing application

A novel chitosan/sodium hyaluronate/iridium (CHI/SH/Ir) hydrogel nanocomposite with a unique microstructure containing vertically aligned pores is fabricated via an electrophoresis technique. The formation of orderly vertical pores in CHI/SH/Ir hydrogel nanocomposite is due to the confinement of hydrogen bubbles produced from the water electrolysis during electrophoresis that limits their lateral movement and coalescence. In a wet state, the diameter for the vertical pores is 600-700 μm. With a thickness of 500 μm, the CHI/SH/Ir hydrogel nanocomposite exhibits a porosity of 76.7 % and a water uptake of 350 %. Its tensile strength is almost doubled to 8.7 MPa, as compared to that of counterpart without the addition of iridium. In CHI/SH/Ir hydrogel nanocomposite, the iridium nanoparticles are homogeneously distributed with an average size of 3 nm. The CHI/SH/Ir electrophoresis suspension exhibits a negligible cytotoxicity. In cell migration test using the human keratinocytes HaCaT cells, the CHI/SH/Ir hydrogel nanocomposite reveals a relative migration of 122.15 ± 9.02 % (p < 0.001) as compared to the blank sample. The presence of vertically aligned pores with the use of SH and iridium nanoparticles indicates a promising opportunity in wound healing application.