Advancing Thermoelectric Performance of Bi₂Te₃ below 400 K

Thermoelectric cooling devices utilizing Bi₂Te₃-based alloys have seen increased utilization in recent years. However, their thermoelectric performance remains inadequate within the operational temperature range (≤400 K), with limited research addressing this issue. In this study, we successfully modulated the carrier concentration of the sample through Te content reduction, consequently lowering the peak temperature of the zT value from 400 to 300 K. This led to a substantial enhancement in thermoelectric performance at room temperature (≤400 K). Furthermore, by doping with La, the electrical transport properties have been further optimized, and the lattice thermal conductivity has been effectively reduced at the same time; the average zT value was ultimately elevated from 0.69 to 0.9 within the temperature range of 300-400 K. These findings hold significant promise for enhancing the efficacy of existing thermoelectric cooling devices based on Bi₂Te₃-based alloys.