Evaluation of incipient enamel-carious-like lesion treated with hydroxyapatite-chitosan nanocomposite hydrogel
Salma M Fathy1, Alsayed Abdelhafez2, Fawzy A Darwesh3
1Dental Biomaterials Department, Faculty of Oral and Dental Medicine, Zagazig University, Zagazig, Egypt; Dental Biomaterials Department, Faculty of Dentistry, Badr University in Cairo, Cairo, Egypt.
Background:
Non-invasive restoration of tooth enamel is a topic of high relevance in dental material science. Multiple approaches have been proposed to reach optimum reconstruction results. The current study was performed to evaluate the cross-sectional microhardness besides mineral quality and content in artificially induced carious enamel after treatment with hydroxyapatite-chitosan (HAp-CS) nanocomposite gel.
Methods:
Artificially carious lesions were induced by immersion of teeth in acidic carboxymethyl cellulose gel (pH 4.95-5) for 24- and 72-hours periods. Two different compositions of HAp-CS nanocomposite hydrogel were prepared with two different ratios 50/50 (%) and 70/30 (%), respectively. Additionally, sodium fluoride gel (1000 ppm concentration) was prepared and used as reference. Gels were applied to carious lesions twice/day for 3 min/each. After 45 days of application, surface morphology, energy dispersive x-ray spectroscopy, micro-Raman analysis in addition to cross-sectional microhardness were evaluated. Statistical analysis was performed using two-way ANOVA and Tukey's post hoc statistical tests.
Results:
Surface morphological evaluation of treated surfaces showed obliteration of surface irregularities. Groups demineralized for 24 hours and treated with 70/30 (HAp-CS) showed highest significant cross-sectional-microhardness (P ≤ 0.05). Evaluated subsurface cross-sectional microhardness showed better mineral quality for groups demineralized for 24 hours and treated with HAp-CS nanocomposite gels.
Conclusions:
Nanocomposite gel with 70/30 (HAp-CS) could efficiently improve cross-sectional microhardness and both minerals composition and quality for lesions demineralized for 24 hours. More severely induced lesions, as demineralized for 72 hours, need more powerful agent compositions and/or prolonged application protocols for improvement.