Natural lignocellulosic biomass structure inspired CNF/Lignin/PBAT composite film with thermoplastic, antibacterial...

The development of a thermoplastic, biodegradable composite material to replace conventional polymers derived from petroleum was the main area of concentration. Herein, a method for preparing antibacterial, UV-blocking and degradable CNF/Lignin/PBAT composite films (CLP) using cellulose nanofibrils (CNF), lignin, and Poly (butylene adipate-terephthalate) (PBAT) as raw materials by solution casting method was described. With the adding of PBAT, the thermal stability, thermoplastic, mechanical properties were enhanced by improving the compatibility between components. The maximum tensile strength of CLP could reach 189.72 MPa, which increased 25.5 % compared to CNF/Lignin film. The average initial decomposition temperature could reach 321 °C, which was much higher than that of CNF and lignin. At the same time, its good heat-sealing performance made it suitable for practical use. Meanwhile, the composite films had excellent UV resistance and could block over 95 % of UV light. The antibacterial results indicated that the films had a good inhibitory effect on E. coli and S. aureus, with a maximum inhibitory ring diameter of 5.56 and 6.36 mm. In addition, the composite film also had excellent barrier capability to liquid and gas. The prepared film had potential to produce flexible packing, industrial compositing and biomedical fields.