Glued-bamboo composite based on a highly cross-linked cellulose-based adhesive and an epoxy functionalized bamboo...

Bamboo, as a renewable bioresource, exhibits advantages of fast growth cycle and high strength. Bamboo-based composite materials are a promising alternative to load-bearing structural materials. It is urgent to develop high-performance glued-bamboo composite materials. This study focused on the chemical bonding interface to achieve high bonding strength and water resistance between bamboo and dialdehyde cellulose-polyamine (DAC-PA_4N) adhesive by activating the bamboo surface. The bamboo surface was initially modified in a directional manner to create an epoxy-bamboo interface using GPTES. The epoxy groups on the interface were then chemically crosslinked with the amino groups of the DAC-PA_4N adhesive, forming covalent bonds within the adhesive layer. The results demonstrated that the hot water strength of the modified bamboo was improved by 75.8 % (from 5.17 to 9.09 MPa), and the boiling water strength was enhanced by 232 % (from 2.10 to 6.99 MPa). The bonding and flexural properties of this work are comparable to those of commercial phenolic resin. The activation modification of the bamboo surface offers a novel approach to the development of low-carbon, environmentally friendly, and sustainable bamboo engineering composites.