Utilizing olive leaves biomass as an efficient adsorbent for ciprofloxacin removal: characterization, isotherm,...

Olive leaves were utilized to produce activated biomass for the removal of ciprofloxacin (CIP) from water. The raw biomass (ROLB) was activated with sodium hydroxide, phosphoric acid, and Dead Sea water to create co-precipitated adsorbent (COLB) with improved adsorption performance. The characteristics of the ROLB and COLB were examined using SEM images, BET surface area analyzer, and ATR-FTIR spectroscopy. COLB has a BET surface area of 7.763 m2/g, markedly higher than ROLB's 2.8 m2/g, indicating a substantial increase in adsorption sites. Through investigations on operational parameters, the optimal adsorption efficiency was achieved by COLB is 77.9% within 60 min, obtained at pH 6, and CIP concentration of 2 mg/mL. Isotherm studies indicated that both Langmuir and Freundlich models fit the adsorption data well for CIP onto ROLB and COLB, with R2 values exceeding 0.95, suggesting effective monolayer and heterogeneous surface adsorption. The Langmuir model revealed maximum adsorption capacities of 636 mg/g for ROLB and 1243 mg/g for COLB, highlighting COLB's superior adsorption capability attributed to its enhanced surface characteristics post-modification. Kinetic data fitting the pseudo-second-order model with R² of 0.99 for ROLB and 1 for COLB, along with a higher calculated q_e for COLB, suggest its modified surface provides more effective binding sites for CIP, enhancing adsorption capacity. Thermodynamic analysis revealed that the adsorption process is spontaneous (∆G^o < 0), and exothermic (∆H^o < 0), and exhibits a decrease in randomness (∆S^o < 0) as the process progresses. The ΔH° value of 10.6 kJ/mol for ROLB signifies physisorption, whereas 35.97 kJ/mol for COLB implies that CIP adsorption on COLB occurs through a mixed physicochemical process.