Bioinspired poly-dopamine/nano-hydroxyapatite: an upgrading biocompatible coat for 3D-printed polylactic acid...

Poly-lactic acid (PLA) has been proposed in dentistry for several regenerative procedures owing to its biocompatibility and biodegradability. However, the presence of methyl groups renders PLA hydrophobic, making the surface less ideal for cell attachment, and it does not promote tissue regeneration. Upgrading PLA with inductive biomaterial is a crucial step to increase the bioactivity of the PLA and allow cellular adhesion. Our purpose is to evaluate biocompatibility, bioactivity, cellular adhesion, and mechanical properties of 3D-printed PLA scaffold coated with poly-dopamine (PDA) and nano-hydroxyapatite (n-HA) versus PLA and PLA/n-HA scaffolds. The fused deposition modelling technique was used to print PLA, PLA with embedded n-HA particles, and PLA scaffold coated with PDA/n-HA by immersion. After matrices characterization for their chemical composition and surface properties, testing the compressive strength was pursued using a universal testing machine. The bioactivity of scaffolds was evaluated by monitoring the formation of calcium phosphate compounds after simulated body fluid immersion. The PLA/PDA/n-HA scaffold showed the highest compressive strength which was 29.11 ± 7.58 MPa with enhancing calcium phosphate crystals deposition with a specific calcium polyphosphate phase formed exclusively on PLA/PDA/n-HA. With cell viability assay, the PDA/n-HA-coated matrix was biocompatible with increase in the IC₅₀, reaching ⁓ 176.8 at 72 without cytotoxic effect on the mesenchymal stem cells, promoting their adhesion and proliferation evaluated by confocal microscopy. The study explored the biocompatibility, bioactivity, and the cell adhesion ability of PDA/n-HA coat on a 3D-printed PLA scaffold that qualifies its use as a promising regenerative material.