Combustion Growth of NiFe Layered Double Hydroxide for Efficient and Durable Oxygen Evolution Reaction

NiFe layered double hydroxide (LDH) with abundant heterostructures represents a state-of-the-art electrocatalyst for the alkaline oxygen evolution reaction (OER). Herein, NiFe LDH/Fe₂O₃ nanosheet arrays have been fabricated by facile combustion of corrosion-engineered NiFe foam (NFF). The in situ grown, self-supported electrocatalyst exhibited a low overpotential of 248 mV for the OER at 50 mA cm^-2, a small Tafel slope of 31 mV dec^-1, and excellent durability over 100 h under the industrial benchmarking 500 mA cm^-2 current density. A balanced Ni and Fe composition under optimal corrosion and combustion contributed to the desirable electrochemical properties. Comprehensive ex-situ analyses and operando characterizations including Fourier-transformed alternating current voltammetry (FTACV) and in situ Raman demonstrate the beneficial role of modulated interfacial electron transfer, dynamic atomic structural transformation to NiOOH, and the high-valence active metal sites. This study provides a low-cost and easy-to-expand way to synthesize efficient and durable electrocatalysts.