Analysis of Tissue Repair of a New Cement Based on Calcium and Strontium Aluminates: A Triple-Blinded, Randomized,...

The focus of this triple-blind randomized study was to evaluate the biocompatibility of a new root canal filling sealer (RCFS) based on tristrontium aluminate and dodecacalcium hepta-aluminate in living tissue.

Forty-five Wistar rats (Rattus norvegicus) were divided into three groups: control (polyethylene), sealer (Bio-C Sealer, Londrina, PR, Brazil), and experimental (tristrontium aluminate and dodecacalcium hepta-aluminate). The tissues were analyzed under an optical microscope to assess different cellular events at different time intervals (7, 15, and 30 days).

Data were analyzed using the Kruskal-Wallis and Dunn (p < 0.05) tests.

In the initial period, a moderate inflammatory infiltrate was observed, similar between the endodontic cements groups (p = 0.725). The intensity of the infiltrate decreased with time, with no significant difference among the groups (p > 0.05). The number of young fibroblasts was elevated in all groups evaluated at 7 days. The experimental group showed the highest number of cells at all time intervals, but the difference with the sealer group at 7 (p = 0.001) and 15 days (p = 0.002) and the control group at 30 days was not significant (p = 0.001). Regarding tissue repair events, the amount of collagen fibers increased over the experimental intervals, with no significant difference between the sealer and control groups (p > 0.05).

The experimental RCFS based on calcium and strontium aluminates proved to be biocompatible for use in close contact with periapical tissue, inducing a low inflammatory reaction and favoring rapid tissue repair.