Ti₃C₂ mediates the NiFe-LDH layered electrocatalyst to enhance the OER performance for water splitting

Oxygen evolution reaction (OER) is a very complex process with slow reaction kinetics and high overpotential, which is the main limitation for the commercial application of water splitting. Thus, it is of necessary to design high-performance OER catalysts. NiFe based layered double hydroxides (NiFe-LDHs) have recently gained a lot of attention due to their high reaction activity and simple manufacturing process. In this study, a novel electrocatalyst based on NiFe-LDH was constructed by introducing Ti₃C₂, which was utilized to modulate the structural and electronic properties of the electrocatalysts. Structural examinations reveal that the Ti₃C₂ of 2D structure successfully dope the NiFe-LDHs nanosheets, forming NiFe-LDH/Ti₃C₂ heterojunctions. Firstly, the heterojunction substantially reduces the charge transfer resistance, promoting the electron migration between the LDH nanosheets. Secondly, theoretical calculations demonstrate that the energy barrier between the rate-determining step from *OH to *O is lowered, favoring the formation of the reaction intermediates and thus the occurrence of OER. As a result, the composite electrocatalyst exhibits a low overpotential of 334 mV at a current density of 10 mA/cm² and a small Tafel slope of 55 mV/dec, which are superior to those of the NiFe-LDH by 11.2 % and 38.5 %, respectively. This study provides inspiration for promoting the performances of NiFe based electrocatalysts by utilizing 2D materials.