Study on the Synthesis of Nano Zinc Oxide Particles under Supercritical Hydrothermal Conditions

The supercritical hydrothermal synthesis of nanomaterials has gained significant attention due to its straightforward operation and the excellent performance of the resulting products. In this study, the supercritical hydrothermal method was used with Zn(CH₃COO)₂·2H₂O as the precursor and deionized water and ethanol as the solvent. Nano-ZnO was synthesized under different reaction temperatures (300~500 °C), reaction times (5~15 min), reaction pressures (22~30 MPa), precursor concentrations (0.1~0.5 mol/L), and ratios of precursor to organic solvent (C₂H₅OH) (2:1~1:4). The effects of synthesis conditions on the morphology and size of ZnO were studied. It was found that properly increasing hydrothermal temperature and pressure and extending the hydrothermal time are conducive to the more regular morphology and smaller size of ZnO particles, which is mainly achieved through the change of reaction conditions affecting the hydrothermal reaction rate. Moreover, the addition of ethanol makes the morphology of nano-zno more regular and significantly inhibits the agglomeration phenomenon. In addition to the change in physical properties of the solvent, this may also be related to the chemical bond established between ethanol and ZnO. The results show that the optimum synthesis conditions of ZnO are 450 °C, 26 MPa, 0.3 mol/L, 10 min, and the molar ratio of precursor to ethanol is 1:3.